Can low-fusing glass application affect the marginal misfit and bond strength of Y-TZP crowns?

Abstract To evaluate the effect of different surface treatments on the marginal misfit and retentive strength between Y-TZP crowns and an epoxy resin. Forty (40) epoxy resin (G10) abutments (height: 5mm, conicity: 60, finish line: large chamfer) with equal dimensions were milled and included in polyurethane to simulate the periodontal ligament. Next, 40 Y-TZP crowns (thickness: 1mm) were milled (Cerec in Lab) and randomly divided into four groups (n=10) according to the surface treatment: GS(glaze spray), GP(glaze powder/liquid), P(zirconia primer) and RS(tribochemical silica coating). The conditioned surfaces were cemented with dual self-adhesive cement, light cured and submitted to thermomechanical cycling (2x106, 100N, 4Hz, 5°/55°C). Marginal misfit was analyzed by a stereomicroscope and SEM. Retentive strength test was performed (1mm/min) until crown debonding. Glaze layer thickness was also performed to GS and GP groups. Marginal misfit data were analyzed by Kruskal Wallis and Dunn tests; one-way ANOVA and Tukey (5%) analyzed the tensile strength data. The marginal misfit of the GS (48.6±19.9μm) and GP (65.4±42.5μm) were statistically lower than the RS (96±62.9μm) and P (156±113.3μm) (p=0.001). The retentive strength of the GP (470.5±104.1N) and GS (416.8±170.2N) were similar to the P (342.1±109.7N), but statistically higher than those of the RS (208.9±110N). The GS and GP glaze layer was 11.64μm and 9.73μm respectively. Thus, glaze application promoted lower marginal discrepancy and higher retentive strength values than conventional techniques.

Estabelecimento de uma proporção entre largura de dentes artificiais anteriores, medidos em curva e em linha reta / Establishing a ratio between the width of anterior artificial teeth measured in curved and straight configurations

Objetivo: estabelecer uma proporção única de redução entre a medida da largura dos seis dentes artificiais anteriores superiores, em curva e em linha reta. Material e métodos: foi utilizado um dispositivo pré-fabricado, simulando o plano de cera superior, no qual foram montados os dentes (Premium, Heraeus-Kulzer Inc. ­ Hanau, Alemanha) nos seguintes modelos: T2, O2, R2, S2, S4, O4, S6, R4, R6, T4 e T6. Em seguida, a largura em curva entre os dentes anteriores montados foi medida com uma régua flexível, tendo como referência a face distal dos caninos. A partir dos dados obtidos (mm) e dos valores das medidas fornecidos na carta molde do fabricante, realizou-se o cálculo da proporção entre essas duas medidas para cada modelo de dentes. Resultados: verificou-se redução entre a medida em curva e a medida em linha reta, variando de 4% a 19% para todos os tipos de modelos estudados. Assim, não foi possível estabelecer uma porcentagem padrão única de redução para todos os tipos de dentes do fabricante. Porém, agrupando-se a redução em milímetros, observou-se uma redução variável entre os modelos em curva e em linha reta: 2 mm para o modelo T2; 3 mm para os modelos O2, R2, S2 e S4; 4 mm para os modelos O4 e S6; 5 mm para os modelos R4, R6 e T4; e 9 mm para o modelo T6. Conclusão: é possível estabelecer uma redução aproximada (em mm) entre uma medição em curva e reta na seleção de dentes artificiais Premium/Heraeus-Kulzer.

Objective: this study aimed to establish a single rate reduction between the measurement of the width of the six artificial anterior upper teeth, in curved and straight configurations. Methods: for this, a prefabricated device simulating the upper wax rim was used and received artificial teeth (Premium, Heraeus-Kulzer Inc., Hanau, Germany) from T2, O2, R2, S2, S3, O4, S6, R4, R6, T4, and T6. Next, the width of the six anterior teeth in curvature was measured from the distal of both canines. After, based on the mold chart of the manufacturer, the ratio between the straight and curved configurations was generated. Results: there was a 4% to 19% in reduction between the curved and straight configurations. A single reduction percentage was not obtained for all tooth forms. However, the reductions were 2 mm for T2, 3 mm for O2, R2, S2 and S4; 4 mm for O4 and S6; 5 mm for R4, R6, and T4; and 9 mm for T6 models. Conclusion: it is possible to establish an approximated reduction (in mm) between the curved and straight configurations for Premium/Heraeus-Kulzer artificial teeth.

Estabilidade de Cor de uma Resina Composta Indireta / Color Stability of an Indirect Composite Resin

A cor das resinas compostas indiretas é um dos mais importantes fatores no sucesso do tratamento protético. Com este material a estabilidade de cor é aspecto preponderante na longevidade deste trabalho. A proposta deste estudo foi avaliar a estabilidade de cor de resina composta indireta (Resilab Master, Wilcos – Brasil) através de um colorímetro digital. Foram confeccionados 32 corpos-de-prova (CP). Realizou-se o registro inicial da cor de cada CP, através de um colorímetro digital, que foram distribuídos em 4 grupos (n=8) e imersos em diferentes soluções. Grupo 1 (controle): água destilada/estufa; Grupo 2: água destilada/termociclagem; Grupo 3 : suco de laranja/termociclagem e Grupo 4: café/termociclagem. Após termociclagem e imersão em estufa (tempo total aproximado de 60 horas), as amostras foram enxaguadas e o registro final da cor foi obtido. Os dados foram submetidos à análise estatística (Teste de Dunnet – p<0,005). Os resultados mostraram que os valores de ΔE (diferença de cor) e desvio padrão dos grupos foram: G1: 2,35±0,84; G2: 2,97±1,21; G3: 8,33±5,87; G4: 22,38±5,33. Foi observado que os grupos 3 e 4 diferiram estatisticamente do grupo 1, exceto o grupo 2 que não foi estatisticamente significante. Baseado nos resultados, conclui-se que a termociclagem contribui para uma alteração de cor da resina composta indireta e a solução de café mancha mais do que o suco de laranja.

Remoção do parafuso de fixação fraturado do implante: relato de caso / Removal of fractured implant abutment screw: a case report

Apesar da reabilitação de pacientes parcial e totalmente edêntulos com implantes osseointegrados ser clinicamente aceitável na Odontologia moderna, muitas falhas ainda podem ocorrer nesse tipo de tratamento protético. Freqüentemente o afrouxamento e fratura dos parafusos de fixação e/ou retenção dos componentes dos implantes serve como um sinal de alerta, indicando que o sistema de conexões necessita de uma reavaliação. Assim, a proposta deste trabalho foi relatar a situação clínica da fratura de um parafuso de fixação e a técnica de remoção do fragmento no interior do implante.